Industrial absorbents and methods of manufacturing the same

ABSTRACT

An industrial absorbent and methods of manufacturing the same. In one embodiment, the industrial absorbent includes a first scrim made from at least one thermoplastic material; a second scrim made from at least one thermoplastic material; and a middle layer positioned between the first and second scrims. The middle layer includes a dry-laid web of fire-retardant treated cellulose and opened, individuated staple bicomponent fiber. At least some of the bicomponent fiber in the middle layer is thermally bonded to at least some of the cellulose in the middle layer, and the first and second scrims are thermally bonded to the middle layer.

BACKGROUND

Embodiments of the invention relate to non-woven materials and, more particularly, to certain types of non-woven materials which are known as industrial absorbents.

Industrial absorbents are used in a variety of circumstances. For example, non-woven absorbent pads are often used in manufacturing facilities to absorb water, oil, chemicals, and other liquids that may be dispensed, emitted, or leaked from various machines and manufacturing lines. For example, industrial absorbent pads may be used around cutting machines to absorb lubricants, printing presses to absorb ink, and processing equipment to absorb chemicals. The pads are used to help reduce the spread of such liquids into walkways, onto other machinery, to pick up spills after they occur, and similar purposes.

SUMMARY

Although current industrial absorbents are functional, industrial absorbents with improved characteristics such as increased absorbency, lower cost, and fire retardancy would be beneficial. Absorbency is often dependent on the bulk-to-weight ratio (or density) of the material. One embodiment of the invention includes an industrial absorbent made mostly from cellulose. The cellulose is processed in such a manner as to increase its bulk or volume, thereby helping to increase absorbency. In some embodiments, the finished industrial absorbent has an absorbency of about 1 to about 2.5 times its own weight and a bulk-to-weight ratio of about 10 to about 30. Another benefit of using cellulose is decreased costs. Most current industrial absorbents are made largely from polypropylene, a petroleum-derived material. Currently, it appears that the costs of petroleum-based products will continue to rise. Thus, reducing the amount of petroleum-based components in the absorbents can help to control costs. In addition, petroleum is considered to be a non-renewable resource. Thus, reducing the amount of petroleum-based components helps reduce dependency on non-renewable resources.

In many instances, cellulose is considered to pose higher fire risks than certain synthetic materials currently used in industrial absorbents. However, the cellulose used in certain embodiments of the invention is treated with a fire retardant to ensure that the end product has a fire retardancy that is equivalent to or better than current industrial absorbents.

Another benefit of certain embodiments of the invention is that scrap cellulose may be used. In many instances, scrap cellulose is available at relatively low cost. Thus, the overall cost of the end product is reduced. In addition, the use or recycling of scrap material may have environmental benefits.

In one embodiment the invention provides an industrial absorbent. The absorbent includes a top scrim made from at least one thermoplastic material, a bottom scrim made from at least one thermoplastic material, and a middle layer positioned between the top and bottom scrims. The middle layer includes a dry-laid web of fire-retardant treated cellulose and opened, individuated, staple bicomponent fiber. At least some of the bicomponent fiber in the middle layer is thermally bonded to at least some of the cellulose in the middle layer. In addition, the first and second scrims are thermally bonded to the middle layer.

Another embodiment of the invention provides a method of manufacturing an industrial absorbent. The method includes obtaining at least one type of cellulose from a group of cellulose sources including a source of virgin cellulose, a source of post-industrial cellulose, and a source of post-consumer cellulose, shredding the cellulose, and declumping and sizing the cellulose. The cellulose is metered into a spray booth where at least one additive is applied to the cellulose. The at least one additive can be selected from the group of a debonder, a colorant, fixant, and a fire retardant. The method also includes drying the cellulose; declumping and sizing the cellulose, fiberizing the cellulose, or both; metering the cellulose into a forming head; metering bicomponent fiber into the forming head; and forming a non-woven web of the cellulose and bicomponent fiber on a forming wire positioned below the forming head. The web is sandwiched between a first scrim and a second scrim to form a non-woven web. The non-woven web is then heated in an oven to cause an outer layer of the bicomponent fiber to melt. The molten material contacts other fiber and when re-hardened or cooled creates bonds between at least some of the bicomponent fiber and the cellulose. The heating process also causes at least a portion of the first and second scrims to bond with the non-woven web. After the non-woven web has been formed and cooled, it is then wound onto a parent roll in a continuous process. These rolls are then taken to a converting process where they are either cut into pads or converted into smaller rolls. It is also possible to replace the parent roll winder with an in-line sheeter to cut the non-woven web into pads as part of a continuous process.

Other aspects and embodiments of the invention will become apparent by consideration of the detailed description and accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective, partially exploded view of an industrial absorbent.

FIG. 2 is a flow chart illustrating a portion of a process for making an industrial absorbent.

FIG. 3 is a flow chart illustrating another portion of a process for making an industrial absorbent.

FIG. 4 is a flow chart illustrating another portion of a process for making an industrial absorbent.

DETAILED DESCRIPTION

Before any embodiments of the invention are explained in detail, it is to be understood that the invention is not limited in its application to the details of construction and the arrangement of components set forth in the following description or illustrated in the following drawings. The invention is capable of other embodiments and of being practiced or of being carried out in various ways.

FIG. 1 illustrates an industrial absorbent pad 10 having a first, non-woven scrim 12, which may be made from one or more thermo-plastic materials such as polyethylene, polypropylene, and polyester. In one embodiment, the scrim 12 is made from spunbond, bicomponent material or fibers. In one common form, bicomponent fibers include an inner core of polypropylene and a sheath or outer layer of polyethylene. The outer sheath of polyethylene has a lower melting point than the core of polypropylene. As will be discussed in greater detail below, the scrim 12 is used as an outer layer for the pad 10 to help increase the tensile strength of the pad 10 and to protect a middle layer 14 of dry-laid material. One way in which the scrim helps protect the middle layer 14 is by preventing or reducing linting of the middle layer.

In one embodiment, the scrim 12 is fixed to the middle layer 14 by thermal bonds. In this instance, the scrim 12 is heated such that the polyethylene in the bicomponent fibers melts and comes into contact with fibers from the middle layer 14. The pad 10 is then cooled (or allowed to cool) so that the polyethylene re-hardens or cools to form bonding points between at least some of the bicomponent fibers in the scrim 12 and the fibers within the middle layer 14.

The middle layer 14 is, in at least one embodiment, comprised of cellulose or cellulose fibers and staple bicomponent fibers. In a preferred embodiment, the middle layer 14 includes about 90% cellulose and about 10% staple bicomponent fibers by weight. The cellulose can be obtained from a number of different sources including virgin cellulose, post-industrial cellulose (for example, scrap from a paper making facility), and post-consumer cellulose (for example, paper and similar materials recycled by individuals).

The pad 10 also includes a second, non-woven scrim 18. The second scrim 18 may be identical to the first scrim 12 and serves a similar purpose as the scrim 12. The second scrim 18 is fixed to the middle layer 14 in a manner similar to how the first scrim 12 is fixed to the middle layer.

FIG. 2 illustrates a process 20 for making the pad 10. The process 20 begins at step or block 22 in which cellulose from a variety of sources, including those described above, is obtained. Prior to being formed (along with bicomponent fiber) into the middle layer 14, the cellulose undergoes a number of processing steps. First, the cellulose is processed (i.e., shredded) in a shredder (block 24) and then declumped and sized in a first hammer mill (block 26). The processed cellulose may then be delivered to a reserve (block 28) to help ensure proper operation of downstream processes. In particular, a reserve may be used to help ensure that material is supplied to downstream processes at a constant or controlled rate.

The cellulose is then provided to a metering device (block 30) to help ensure the delivery of proper amounts of cellulose to downstream processes. In the embodiment shown, the cellulose is metered into a spray booth or similar device (block 34) (generically, an inline treatment process). A variety of liquid and dry additives may be added to the cellulose in the spray booth (or other treatment device) including fire retardants 36, colorants 38, colorant fixants, and debonders 40. The debonder (which may sometimes be a surfactant) diminishes and inhibits the formation of hydrogen bonds, which increases bulk and absorbency of the end product.

The purpose of colorant fixants, for example, is to reduce running or bleeding of the colorant added to the cellulose. In the embodiment shown in FIG. 2, the additives are metered into the spray booth through a metering unit (block 44). One manner of applying fire retardant and additives to the cellulose that may be useful in embodiments of the present invention is described in U.S. Pat. No. 5,534,301, which is assigned to one of the inventors of the present application.

After being treated in the spray booth, the cellulose is dried in a dryer (block 48). The dried cellulose is then provided to a second hammer mill, a fiberizer, or both as shown by blocks 52 and 54 and directional paths 56, 58, and 60. The hammer mill is useful for breaking up the cellulose into small pieces and the fiberizer is useful for individuating the fibers to increase the bulk-to-weight ratio. Thus, one purpose of the post-drying process is to break up clumps of cellulose that may have been formed when the cellulose is in the spray booth. In addition, the post-drying process helps individuate the cellulose fibers before the cellulose is delivered to a forming head (discussed below).

After the cellulose is processed in the second hammer mill, the fiberizer, or both, the cellulose is provided to a forming head of a dry-laid or air-laid device. Before being sent to the forming head, the cellulose may be provided to a second volumetric reserve (block 66) to control the rate of delivery of material. In addition, the cellulose, the bicomponent fiber, or both may be passed through a corona unit, which acts to electrically charge the cellulose and bicomponent fibers, as applicable (block 68). Electrically charging the bicomponent and cellulose fiber can help in increasing tensile strength of the non-woven web, for example, causing the fibers to hold onto or be attracted to other materials. Once appropriately processed, the cellulose is provided via an air stream to a chute with a metering device on top of the forming head (block 70). The cellulose is then air drafted into a rectangular head of the forming head (block 71). As the cellulose travels through ducts to the chute and into the forming head, the individuated cellulose fibers may reform into clumps. The forming head breaks up these clumps of cellulose (block 72) and deposits the cellulose fibers on a wire or conveyor (often referred to as a forming table) (block 73). The first scrim 12 is unwound (block 74) so that it may be provided to the forming table in a manner such that an air-laid web is formed on top of the scrim 12. If desired, the first scrim 12 may be processed in a corona unit (block 75) before it reaches the forming table. Processing the scrim 12 in the corona unit helps to increase adhesion of the scrim 12 to the layer 14. As will be discussed later, the cellulose is mixed with bicomponent fiber in the forming head. Thus, the air-laid web (or middle layer 14) formed on the forming table includes a mixture of cellulose fibers (processed and treated as described above) and bicomponent fiber (processed as described below).

After the web is formed on the first scrim 12, the second scrim 18 is applied to the top of the web. In particular, the scrim 18 may be unwound (block 76), processed in a corona unit (block 77), and placed on top of the web formed on the forming table. Once the three layers of the pad 10 have been positioned correctly with respect to one another, the scrims 12 and 18 and the middle layer 14 can be bonded together. In addition, the cellulose material in the middle layer 14 may be bonded together. In one embodiment, the non-woven web 10 is passed through a transfer station (block 78) and subsequently through an oven, which can take the form of a conventional thermal oven or a radio frequency (“RF”) or microwave oven (blocks 80 and 82). While in the oven, the bicomponent fibers in the scrims 12 and 18 and the bicomponent fibers in middle layer 14 melt. As a consequence, thermal bonds are formed between the scrims 12 and 18 and the middle layer 14 and within the middle layer 14. (The bonds are formed in a manner as was described above with respect to scrim 12). After being heated in the oven, the non-woven web 10 may be processed in a pin roll bonding station, if desired (block 84). A pin roll creates dimples in the non-woven web 10 and these dimples help to mechanically hold the layers of the non-woven web 10 together. The pin roll station may include one or more pin rolls.

Once the pad is bonded and optionally dimpled, it may be wound on a winder (block 86). Rolls of pad material may be converted in a separate process such that the pad material is cut to desired sizes and packaged in containers suitably designed to enable easy dispensing of individual pads by end users. Alternatively, the pad material may be wound on smaller rolls or cut, inline, into pads suitable for sale to end users.

As noted, bicomponent fiber is provided to the forming head. In one embodiment, the bicomponent fibers are staple bicomponent fibers. In certain embodiments fibers of about 1 to 10 denier (thickness) and lengths of about ⅛″ to about 4″ can be used. FIG. 4 illustrates a process 100 by which bicomponent fiber is processed and supplied to the forming head. First, bulk bicomponent fiber (usually in the form of bales) (block 102) is supplied to a feed apron (block 104). Prior to supplying the bales to the feed apron, the straps or wires holding the bales are removed. The feed apron moves the bales of bicomponent fiber to a pre-opener (block 106). The pre-opener breaks the bails into pieces and transfers metered amounts of bicomponent fibers to an opener (block 110). The opener breaks apart the pieces of bicomponent material so as to open and individuate the fibers. If desired the individuated fibers may be transferred to a volumetric reserve (block 112) to help control the rate of fiber delivery to downstream processes. In addition, the bicomponent fiber may also be passed through a corona unit (block 113). Fiber is transported via an air stream from the volumetric reserve to a chute above the forming head (block 114). High velocity ductwork entrains the fiber in an air stream, which carries the fiber into the forming head (block 118). The bicomponent fiber is mixed with the cellulose fibers in the forming head (block 120). As described above, an air- or dry-laid web of cellulose and bicomponent fibers is created by the forming head. A forming head suitable for use in making the pad 10 is described in U.S. patent application Ser. No. 11/296,125, which is owned by the same assignee of the present application.

If desired, the bicomponent fiber may be treated with a surfactant. When so treated, the bicomponent fiber becomes hydrophilic. The surfactant also helps to increase bulk and absorbency.

What has been described with respect to process 20 and process 100 involves the use of separate chutes to deliver fibers to a forming head: a first chute provides cellulose fibers to the forming head and a second chute provides bicomponent fibers to the forming head. In addition to the two-chute process, it is possible to use a single chute into which both cellulose and bicomponent fiber are placed. In addition, the chute or chutes do not need to be placed on top of the forming head. For example, fiber may be entrained in an air (generically, fluid) stream within a venturi type duct that leads into the forming head.

As should be apparent from the above, embodiments of the invention provide, among other things, industrial absorbents and methods of manufacturing the same. Various features, advantages, and embodiments of the invention are set forth in the following claims. 

1. An industrial absorbent comprising: a first scrim made from at least one thermoplastic material; a second scrim made from at least one thermoplastic material; and a middle layer positioned between the first and second scrims, the middle layer having a dry-laid web of fire-retardant treated cellulose and opened, individuated staple bicomponent fiber, wherein at least some of the bicomponent fiber in the middle layer is thermally bonded to at least some of the cellulose in the middle layer, and at least the first and second scrims are thermally bonded to the middle layer.
 2. An industrial absorbent as claimed in claim 1, wherein the fire-retardant treated cellulose includes cellulose treated with a debonder.
 3. An industrial absorbent as claimed in claim 2, wherein the fire-retardant treated cellulose includes a colorant.
 4. An industrial absorbent as claimed in claim 3, wherein the fire-retardant treated cellulose includes a colorant fixant.
 5. An industrial absorbent as claimed in claims 1, 2, or 3, wherein the first and second scrims include spunbond, bicomponent material.
 6. An industrial absorbent as claimed in claim 1, wherein the middle layer includes a mixture of about 90% of cellulose and about 10% of bicomponent fiber, by weight.
 7. An industrial absorbent as claimed in claim 1, wherein the middle layer has a bulk-to-weight ratio of about 10 to about
 30. 8. An industrial absorbent as claimed in claim 1 having an absorbency of about 1 to about 2.5 times its own weight.
 9. An industrial absorbent as claimed in claim 1, where in the cellulose includes waste cellulose.
 10. A method of manufacturing an industrial absorbent, the method comprising: obtaining at least one type of cellulose from a group of cellulose sources including a source of virgin cellulose, a source of post-industrial cellulose, and a source of post-consumer cellulose; shredding the cellulose; declumping and sizing the cellulose; metering the cellulose into a spray booth; applying at least one additive to the cellulose in the spray booth, the at least one additive selected from the group of a debonder, a colorant, a fixant, and a fire retardant; if the at least one additive is a liquid, drying the cellulose; declumping and sizing the cellulose, fiberizing the cellulose, or both; metering the cellulose into a forming head; metering bicomponent fiber into the forming head; forming a web of the cellulose and bicomponent fiber on a forming wire positioned below the forming head; sandwiching the web between a first scrim and a second scrim to form a pad; and heating the pad in an oven to cause an outer layer of the bicomponent fiber to melt to bond at least some of the bicomponent fiber to at least some of the cellulose and to cause at least a portion of the first and second scrims to bond with the web.
 11. A method as claimed in claim 10, further comprising milling the cellulose to individuate cellulose fibers.
 12. A method as claimed in claim 10, wherein heating the pad in an oven includes heating the pad in an RF unit.
 13. A method as claimed in claim 10, wherein heating the pad in an oven includes heating the pad in a thermal oven.
 14. A method as claimed in claim 10, further comprising processing the cellulose in a corona unit prior to metering the cellulose into a forming head.
 15. A method as claimed in claim 10, further comprising processing the bicomponent staple fiber in a corona unit prior to metering the bicomponent fiber into a forming head.
 16. A method as claimed in claim 10, further comprising processing the first scrim in a corona unit prior to sandwiching the web of the cellulose and bicomponent fiber.
 17. A method as claimed in claim 10, further comprising placing the first scrim on the forming wire and forming a web of the cellulose and bicomponent fiber on the first scrim.
 18. A method as claimed in claim 10, further comprising processing the second scrim in a corona unit prior to sandwiching the web of the cellulose and bicomponent fiber.
 19. A method as claimed in claim 10, further comprising processing the pad in a pin roll station after heating the pad in an oven.
 20. A method as claimed in claim 10, wherein metering the cellulose into a forming head and metering bicomponent fiber into the forming head include entraining the cellulose and bicomponent fiber via a venturi effect in to a single chute.
 21. A method as claimed in claim 10, wherein metering the cellulose into a forming head includes entraining the cellulose via an air stream into a first chute and metering bicomponent fiber into the forming head include entraining the bicomponent fiber via an air stream into a second chute.
 22. A method as claimed in claim 10, further comprising treating the cellulose with a debonder, a surfactant, or both.
 23. A method of manufacturing an industrial absorbent, the method comprising: obtaining at least one type of cellulose from a group of cellulose sources including a source of virgin cellulose, a source of post-industrial cellulose, and a source of post-consumer cellulose; shredding the cellulose; declumping and sizing the cellulose; applying at least one liquid additive to the cellulose, the at least one liquid additive selected from the group of a debonder, a colorant, a fixant, and a fire retardant; drying the cellulose; individuating the cellulose, the bicomponent fiber, or both; supplying the cellulose and bicomponent fiber to a forming head; forming a web of the cellulose and bicomponent fiber on a forming wire positioned below the forming head; sandwiching the web between a first scrim and a second scrim to form a pad; and heating the pad in an oven to cause an outer layer of the bicomponent fiber to melt to bond at least some of the bicomponent fiber to at least some of the cellulose and to cause at least a portion of the first and second scrims to bond with the web.
 24. An industrial absorbent comprising: a first scrim made from at least one thermoplastic material; a second scrim made from at least one thermoplastic material; and a middle layer positioned between the first and second scrims, the middle layer having a dry-laid web of cellulose and opened, individuated staple bicomponent fiber, wherein at least some of the bicomponent fiber in the middle layer is thermally bonded to at least some of the cellulose in the middle layer, and at least the first and second scrims are thermally bonded to the middle layer. 